Precautions for aluminum profile processing: temperature
During the processing process, temperature setting and control are very important. There is a certain temperature difference between the processing temperature and the surface temperature of the material. Therefore, when setting the temperature, it is necessary to set it according to the actual temperature of the furnace. Throughout the entire process, close attention should be paid to temperature changes, and temperature fluctuations should be monitored in real-time to avoid problems caused by temperature differences, Causing adverse effects on the finished product.
Aluminum profile processing precautions 2: aging
Aging is a common method of heat treatment for aluminum alloys. If it is at room temperature, it is natural aging, and if it is above room temperature, it is artificial aging. Aging treatment can improve the mechanical properties of aluminum processed products and also improve the physical and chemical properties of aluminum. When conducting aging treatment, certain insulation measures should be taken, and of course, special attention should be paid to the insulation time. The insulation time should be appropriate to prevent the hardness of the aluminum material from being insufficient after too short or too long.
Aluminum profile processing precautions three: furnace loading
Before charging aluminum profile products, special alloys and ordinary alloys must be separated. If special processing conditions are encountered, special alloys need to be taken out for aging treatment.
Aluminum profile processing precautions 4: extrusion
The extrusion process is also a very important part of aluminum processing. When squeezing and framing, it is necessary to pay attention not to be too dense, and there must be a certain spacing between materials. Aluminum products produced through extrusion processing generally have a low hardness before aging treatment and cannot be used as finished products. Therefore, in general, it is necessary to age treat the extruded aluminum profile to improve its strength